Semiconductor device and a method of manufacturing the same

ABSTRACT

Provided is a method of manufacturing a semiconductor device having an n-type FET and a p-type EFT each formed over a semiconductor substrate, which comprises (a) forming, over the n-type FET and p-type FET, a first insulating film for generating a tensile stress in the channel formation region of the n-type FET so as to cover gate electrodes of the FETs, while covering, with an insulating film, a semiconductor region between the gate electrode of the p-type FET and an element isolation region of the semiconductor substrate; (b) selectively removing the first insulating film from the upper surface of the p-type FET by etching; (c) forming, over the n-type and p-type FETs, a second insulating film for generating a compressive stress in the channel formation region of the p-type FET so as to cover the gate electrodes of the FETs; and (d) selectively removing the second insulating film from the upper surface of the n-type FET. The present invention makes it possible to simultaneously increase the drain currents of the n-type FET and p-type FET (improve current driving capacity).

TECHNICAL FIELD

[0001] The present invention relates to a semiconductor device and a manufacturing method thereof, particularly, to a semiconductor device having, on the same substrate thereof, both an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, and a technique effective when adapted to a manufacturing technique of the device.

BACKGROUND OF THE INVENTION

[0002] As a field effect transistor installed on a semiconductor device, an insulated gate field effect transistor called “MISFET” (Metal Insulator Semiconductor Field Effect Transistor) is known. Owing to the feature of this MISFET that it readily enables high integration, it is used widely as a circuit element constituting an integrated circuit.

[0003] Irrespective of an n-channel conductivity type or p-channel conductivity type, MISFET usually has a channel formation region, a gate insulating film, a gate electrode, a source region and a drain region. The gate insulating film is disposed in an element formation region on the circuit formation surface (on main surface) of a semiconductor substrate and it is formed, for example, of a silicon oxide film. The gate electrode is disposed over the element formation region of the circuit formation surface of the semiconductor substrate via the gate insulating film, and it is formed, for example, of a polycrystalline film having a resistance reducing impurity introduced therein. The channel formation region is disposed in a region (just below the gate electrode) of the semiconductor substrate opposite to the gate electrode. The source and drain regions are formed in semiconductor regions (impurity diffused regions) which are disposed on both sides of the channel formation region in the channel length direction.

[0004] MISFET having, as a gate insulating film, a silicon oxide film is usually called “MOSFET” (Metal Oxide Semiconductor Field Effect Transistor). The term “channel formation region” means a region in which a current passage (channel) connecting the source region and drain region is to be formed. MISFET permitting a current flow in the thickness direction (depth direction) of the semiconductor substrate is called “vertical type”, while MISFET permitting a current flow in the plane direction (surface direction) is called “horizontal type”. MISFET permitting formation of a channel of electrons (conduction path) in the channel formation region between the source region and drain region (below the gate electrode) is called n-type (or n-channel conductivity type), while that permitting formation of a channel of an electron hole is called p-type (or p-channel conductivity type).

SUMMARY OF THE INVENTION

[0005] In the ultrafine CMIS (Complementary MIS) process in the 0.1 micron generation, temperature has come to be set lower because of the introduction of a new material and suppression of a short channel effect of MISFET. This tends to leave a process-induced residual strain in the element. The process-induced residual stress works on the surface layer portion of the circuit formation surface of a semiconductor substrate, that is, the channel formation region of MISFET.

[0006] In the ordinarily employed CMIS (complementary MIS) process, a material used for the formation of an interlayer insulating film over the circuit formation surface of a semiconductor substrate is not made different between the n-channel conductivity type MISFET and p-channel conductivity type MISFET. As a result, their stresses working on the channel formation region are substantially equal in one chip. It is the common practice to make a process-wise device in order to reduce the stress working on the channel formation regions of the n-channel conductivity type MISFET and p-channel conductivity type MISFET.

[0007] With regards to a change in the transistor characteristics depending on the stress of a channel formation region, when the stress is applied in a direction similar to that of the flow of a drain current (Id) (gate length direction), it is known that:

[0008] (1) the drain current of an n-channel conductivity type MISFET decreases owing to a compressive stress, while increases owing a tensile stress, and

[0009] (2) the drain current of a p-channel conductivity type MISFET increases by a compressive stress, while decreases by a tensile stress.

[0010] The change was however only several % or less (refer to the literature: IEEE TRANSACTIONS ON ELECTRON DEVICES, 38(4) APRIL, p898-900(1991)). In the process generation of a gate length size of 1 μm, such a small percentage partly owes to sufficient annealing at high temperatures for long hours.

[0011] The investigation by the present inventors have revealed that when the gate length of MISFET is miniaturized as small as 0.1 μm or so and the process is conducted at low temperatures, the residual stress heightens and the stress in the channel formation region has a large influence on the characteristics of a transistor.

[0012] For example, when a plasma CVD nitride film (a nitride film formed by plasma CVD) for self aligning contact, which film also serves as an interlayer insulating film, is formed under conditions varied after the formation of MISFET, the stress in the film shows a change from a compressive direction toward a tensile direction, leading to a great change in the transistor characteristics of MISFET. This change is shown in FIG. 2 as dependence of drain current variation (%) on film stress. The value of the stress in the drawing is not an internal stress of the channel formation region of MISFET but is the value of the interlayer insulating film itself found in terms of the warpage of the wafer after covered with the interlayer insulating film.

[0013] The influence of the stress shows a similar tendency to that in the above-described literature, but the percent variation of a drain current is ±10 to 20%, a single digit increase. Depending on the stress of a film, the drain current of the n-channel conductivity type MISFET and that of the p-channel conductivity type MISFET show opposite tendencies. In short, when the former increases, the latter decreases, and vice versa.

[0014] Accordingly, as the intensity of the internal stress changes with the forming conditions of an interlayer insulating film, the drain current of the n-type conductivity type MISFET and that of the p-type conductivity type MISFET exhibit opposite movements each other. A simultaneous improvement in the drain currents of both elements cannot be accomplished.

[0015] On and after the 0.1 micron generation, a variation percentage in the drain current due to this tress reaches ±10 to 20% or greater, causing a change in the balance of the drain currents of the n-channel conductivity type MISFET and p-channel conductivity type MISFET.

[0016] An object of the present invention is therefore to provide a technique capable of increasing the drain current of each of the n-channel conductivity type MISFET and p-channel conductivity type MISFET (increasing the current driving capacity).

[0017] Another object of the present invention is to provide a technique enabling free setting of a drain current ratio between the n-channel conductivity type MISFET to that of the p-channel conductivity type MISFET.

[0018] Of the inventions disclosed by the present application, the outline of a typical one will next be descried briefly.

[0019] The gist of the present invention resides in the control, by the stress of the film, of a stress working on the channel formation region of each of the n-channel conductivity type MISFET and the p-channel conductivity type MISFET so as to increase their drain current. In the n-channel conductivity type field effect transistor, when a tensile stress works, along the flow direction of a drain current (gate length direction), on the channel formation region, a drain current increases. In the p-channel conductivity type field effect transistor, when a compressive stress works, along the flow direction of a drain current (gate length direction), on the channel formation region, a drain current increases. In other words, the stress of a film is utilized to control a tensile stress in the drain current direction to work on the channel formation region of the n-channel conductivity type field effect transistor, and a compressive stress in the drain current direction to work on the channel formation region of the p-channel conductivity type field effect transistor. It can be attained, for example, by the below-described method or device.

[0020] (1) A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor each formed over a semiconductor substrate, which comprises:

[0021] (a) forming, over the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, a first insulating film for generating a tensile stress in the channel formation region of the n-channel conductivity type field effect transistor so as to cover gate electrodes of these transistors, while covering, with an insulating film, a semiconductor region between the gate electrode of the p-channel conductivity type field effect transistor and an element isolation region of the semiconductor substrate;

[0022] (b) selectively removing the first insulating film over the p-channel conductivity type field effect transistor by etching;

[0023] (c) forming, over the n-channel conductivity type field effect transistor and the p-channel conductivity type field effect transistor, a second insulating film for generating a compressive stress in the channel formation region of the p-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors; and

[0024] (d) selectively removing the second insulating film over the n-channel conductivity type field effect transistor.

[0025] (2) A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor each formed over a semiconductor substrate, which comprises:

[0026] (a) forming, over the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, a first insulating film for generating a compressive stress in the channel formation region of the p-channel conductivity type field effect transistor so as to cover gate electrodes of the transistors, while covering, with an insulating film, a semiconductor region between the gate electrode of the n-channel conductivity type field effect transistor and an element isolation region of the semiconductor substrate;

[0027] (b) selectively removing the first insulating film over the n-channel conductivity type field effect transistor by etching;

[0028] (c) selectively forming, over the n-channel conductivity type field effect transistor and the p-channel conductivity type field effect transistor, a second insulating film for generating a tensile stress in the channel formation region of the n-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors; and

[0029] (d) selectively removing the second insulating film over the p-channel conductivity type field effect transistor.

[0030] (3) The method described above in (1) or (2) wherein:

[0031] the insulating film covering the semiconductor region includes sidewall spacers formed on the sidewalls of each of the gate electrodes and a deposited film formed to cover the sidewall spacers.

[0032] (4) The method described above in (1) or (2) wherein:

[0033] the insulating film covering the semiconductor region includes sidewall spacers formed on the sidewalls of each of the gate electrodes and a deposited film formed to cover the sidewall spacers; and

[0034] over the surface of the semiconductor region, a metal-semiconductor reacted layer formed in alignment with the sidewall spacers is disposed.

[0035] (5) The method described above in (1) or (2) wherein:

[0036] the insulating film covering the semiconductor region includes sidewall spacers formed on the sidewalls of each of the gate electrodes and a thermally oxidized film formed between the sidewall spacers and the element isolation region.

[0037] (6) The method described above in (1) or (2) wherein:

[0038] the insulating film covering the semiconductor region includes sidewall spacers formed on the sidewalls of each of the gate electrodes and a thermally oxidized film formed between the sidewall spacers and the element isolation region; and

[0039] over the surface of the semiconductor region, a metal-semiconductor reacted layer formed in alignment with the sidewall spacers is disposed.

[0040] (7) The method described above in (1) or (2) wherein:

[0041] the first and second insulating films are each a silicon nitride film formed by the LP-CVD (Low Pressure-Chemical Vapor Deposition) method, plasma CVD method, or single-wafer thermal CVD method.

[0042] (8) A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor each formed over a semiconductor substrate, which comprises:

[0043] (a) forming first sidewall spacers over a semiconductor region between each of gate electrodes of the n channel conductivity type and p channel conductivity type field effect transistors and an element isolation region of the semiconductor substrate;

[0044] (b) forming, over the surface of the semiconductor region, a metal-semiconductor reacted layer in alignment with the first sidewall spacers;

[0045] (c) forming second sidewall spacers over the metal-semicondutor reacted layer in alignment with the first sidewall spacers,

[0046] (d) forming, over the n-channel conductivity type and p-channel conductivity type field effect transistors, a first insulating film for generating a tensile stress in the channel formation region of the n-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors;

[0047] (e) selectively removing the first insulating film over the p-channel conductivity type field effect transistor by etching;

[0048] (f) forming, over the n-channel conductivity type field effect transistor and the p-channel conductivity type field effect transistor, a second insulating film for generating a compressive stress in the channel formation region of the p-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors; and

[0049] (g) selectively removing the second insulating film over the n-channel conductivity type field effect transistor.

[0050] (9) A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, which comprises:

[0051] (a) forming first sidewall spacers over a semiconductor region between each of gate electrodes of the n channel conductivity type and p channel conductivity type field effect transistors and an element isolation region of the semiconductor substrate;

[0052] (b) forming, over the surface of the semiconductor region, a metal-semiconductor reacted layer in alignment with the first sidewall spacers;

[0053] (c) forming second sidewall spacers over the metal-semicondutor reacted layer in alignment with the first sidewall spacers,

[0054] (d) forming, over the n-channel conductivity type and p-channel conductivity type field effect transistors, a first insulating film for generating a compressive stress in the channel formation region of the p-channel conductivity type field effect transistor so as to cover gate electrodes of the transistors;

[0055] (e) selectively removing the first insulating film over the n-channel conductivity type field effect transistor by etching;

[0056] (f) forming, over the n-channel conductivity type field effect transistor and the p-channel conductivity type field effect transistor, a second insulating film for generating a tensile stress in the channel formation region of the n-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors; and

[0057] (g) selectively removing the second insulating film over the p-channel conductivity type field effect transistor.

[0058] (10) The method described above in (8) or (9) wherein:

[0059] the first and second insulating films are each a silicon nitride film formed by the LP-CVD method, plasma CVD method, or single-wafer thermal CVD method.

[0060] (11) A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, which comprises:

[0061] (a) forming a first insulating film having a tensile stress over the n-channel conductivity type field effect transistor and the p-channel conductivity type field effect transistor so as to cover the gate electrode of each of the transistors,

[0062] (b) forming a second insulating film having a compressive stress greater in terms of absolute value than a tensile stress of the first insulating film over the n-channel conductivity type field effect transistor and the p-channel conductivity type field effect transistor so as to cover the gate electrode of each of the transistors; and

[0063] (c) selectively removing the second insulating film over the n-channel conductivity type field effect transistor by etching.

[0064] The compressive stress of the second insulating film is at least twice as much as the tensile stress of the first insulating film.

[0065] The first and second insulating films are each a silicon nitride film formed by the LP-CVD method, plasma CVD method, or single-wafer thermal CVD method.

[0066] (12) A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, which comprises:

[0067] (a) forming a first insulating film having a compressive stress over the n-channel conductivity type field effect transistor and the p-channel conductivity type field effect transistor so as to cover the gate electrode of each of the transistors,

[0068] (b) forming a second insulating film having a tensile stress greater in terms of absolute value than a compressive stress of the first insulating film over the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor so as to cover the gate electrode of each of the transistors; and

[0069] (c) selectively removing the second insulating film over the p-channel conductivity type field effect transistor by etching.

[0070] The tensile stress of the second insulating film is at least twice as much as the compressive stress of the first insulating film.

[0071] The first and second insulating films are each a silicon nitride film formed by the LP-CVD method, plasma CVD method, or single-wafer thermal CVD method.

[0072] (13) A semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, which comprises:

[0073] a first insulating film having a tensile stress and being formed over the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors, and

[0074] a second insulating film having a compressive stress greater in terms of absolute value than a tensile stress of the first insulating film and being formed over the p-channel conductivity type field effect transistor so as to selectively cover the gate electrode thereof.

[0075] The tensile stress of the second insulating film is at least twice as much as the compressive stress of the first insulating film.

[0076] The first and second insulating films are each a silicon nitride film formed by the LP-CVD method, plasma CVD method, or single-wafer thermal CVD method.

[0077] (14) A semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, which comprises:

[0078] a first insulating film having a compressive stress and being formed over the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors, and

[0079] a second insulating film having a tensile stress greater in terms of absolute value than the compressive of the first insulating film and being formed over the n-channel conductivity type field effect transistor so as to selectively cover the gate electrode thereof.

[0080] The tensile stress of the second insulating film is at least twice as much as the compressive stress of the first insulating film.

[0081] The first and second insulating films are each a silicon nitride film formed by the LP-CVD method, plasma CVD method, or single-wafer thermal CVD method.

[0082] (15) A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor each formed over a semiconductor substrate, which comprises:

[0083] forming an insulating film having a tensile stress over the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors, and

[0084] introducing an element into the insulating film over the p-channel conductivity type field effect transistor, thereby converting the insulating film into a film capable of generating a compressive stress in the channel formation region of the p-channel conductivity type field effect transistor.

[0085] The element is same with an element contained in the insulating film.

[0086] The introduction of the element is conducted by ion implantation of the element perpendicularly to the substrate or ion implantation of the element obliquely to the substrate.

[0087] The insulating film is a silicon nitride film formed by the LP-CVD method, plasma CVD method, or single-wafer thermal CVD method.

[0088] (16) A semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor each formed over a semiconductor substrate, which comprises:

[0089] a film formed over the n-channel conductivity type and p-channel conductivity type field effect transistors so as to cover the gate electrode thereof,

[0090] the film having a first portion having a film stress for generating a tensile stress in the channel formation region of the n-channel conductivity type field effect and a second portion having a film stress for generating a compressive stress in the channel formation region of the p-channel conductivity type field effect transistor.

[0091] The second portion of the film has a higher element concentration than the first portion.

[0092] The film is a silicon nitride film formed by the LP-CVD method, plasma CVD method, or single-wafer thermal CVD method.

[0093] According to the above-described methods, a tensile stress and a compressive stress are applied to the channel formation regions of the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, respectively, resulting in an increase in a drain current of each of the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, depending on the intensity of the stress working on each of the channel formation regions of the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, as illustrated in FIG. 2.

[0094] The stresses working on the channel formation regions of the n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor respectively, making it possible to freely control a drain current ratio of the n-channel conductivity type field effect transistor to the p-channel conductivity type field effect transistor.

[0095] The above-described film is an insulating film made of a silicon nitride film for self-aligning contact (SAC).

[0096] (17) A semiconductor device, which comprises:

[0097] a first field effect transistor formed over a semiconductor substrate and having a silicide layer over a semiconductor region between sidewall spacers disposed on the sidewalls of the gate electrode of said first transistor and an element isolation region of said semiconductor substrate;

[0098] a second field effect transistor formed over said semiconductor substrate and having no silicide layer over a semiconductor region between sidewall spacers disposed on the sidewalls of the gate electrode of said second transistor and an element isolation region of said semiconductor substrate,

[0099] a first insulating film for generating a stress in the channel formation region of said first field effect transistor and formed over said first field effect transistor so as to cover the gate electrode thereof, and

[0100] a second insulating film for generating a stress in the channel formation region of said second field effect transistor and formed over said second field effect transistor so as to cover the gate electrode thereof, wherein:

[0101] between the semiconductor region of said second field effect transistor and said second insulating film, a third insulating film is disposed; and

[0102] between the silicide layer of said first field effect transistor and said first insulating film, said third insulating film is not disposed.

[0103] The followings are definitions of some terms used herein.

[0104] The term “tensile stress working on the channel formation region of a field effect transistor” means a stress at which the lattice constant of Si exceeds its equilibrium in the case where the channel formation region is silicon (Si).

[0105] The term “compressive stress working on the channel formation region of a field effect transistor” means a stress at which the lattice constant of Si becomes below its equilibrium in the case where the channel formation region is silicon (Si).

[0106] The term “tensile stress of a film” means a stress which generates a tensile stress in the channel formation region of a field effect transistor.

[0107] The term “compressive stress of a film” means a stress which generates a compressive stress in the channel formation region of a field effect transistor.

[0108] The gist of the present invention therefore resides in that the interatomic distance of silicon atoms in the channel formation region differs between the n-channel conductivity type field effect transistor and the p-channel conductivity type field effect transistor, in other words, they are different in the size of distortion; and that the interatomic distance of silicon atoms is greater in the channel formation region of the n-channel conductivity type field effect transistor than in the channel formation region of the p-channel conductivity type field effect transistor.

[0109] The above-described objects, the other objects and novel features of the present invention will be apparent from the description herein and accompanying drawings.

[0110] The present inventors have found novel problems during the development of the present invention. These problems will be described later together with Embodiments to which the present invention is applied.

BRIEF DESCRIPTION OF THE DRAWINGS

[0111]FIG. 1 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 1 of the present invention;

[0112]FIG. 2 is a characteristic chart showing dependence, on film stress, of a percent variation in drain current,

[0113]FIG. 3 is a schematic cross-sectional view illustrating the relationship between a current direction and a film stress direction;

[0114]FIG. 4 is a schematic plane view illustrating the relationship between a current direction and a film stress direction;

[0115]FIG. 5 is a schematic cross-sectional view of a semiconductor device of Embodiment 1 of the present invention at a manufacturing step thereof;

[0116]FIG. 6 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 5;

[0117]FIG. 7 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 6,

[0118]FIG. 8 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 7;

[0119]FIG. 9 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 8;

[0120]FIG. 10 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 9;

[0121]FIG. 11 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 10;

[0122]FIG. 12 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 11;

[0123]FIG. 13 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 12;

[0124]FIG. 14 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 13;

[0125]FIG. 15 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 14;

[0126]FIG. 16 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 15;

[0127]FIG. 17 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 16;

[0128]FIG. 18 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 17;

[0129]FIG. 19 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 18;

[0130]FIG. 20 is a schematic cross-sectional view for explaining a problem found by the present inventors during the development of the present invention;

[0131]FIG. 21 is a schematic cross-sectional view for explaining another problem found by the present inventors during the development of the present invention;

[0132]FIG. 22 is a schematic cross-sectional view for explaining a further problem found by the present inventors during the development of the present invention;

[0133]FIG. 23 is a schematic cross-sectional view for explaining a still further problems found by the present inventors during the development of the present invention;

[0134]FIG. 24 is a schematic cross-sectional view illustrating a modification example of Embodiment 1 of the present invention;

[0135]FIG. 25 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 2 of the present invention;

[0136]FIGS. 26A and 26B are each a schematic cross-sectional view illustrating the semiconductor device of Embodiment 2 at a manufacturing step thereof;

[0137]FIG. 27 is a schematic cross-sectional view illustrating the semiconductor device of Embodiment 2 at another manufacturing step thereof;

[0138]FIG. 28 is a schematic cross-sectional view of a semiconductor device according to Embodiment 3 of the present invention at a manufacturing step thereof;

[0139]FIG. 29 is a schematic cross-sectional view of a semiconductor device according to Embodiment 4 of the present invention at a manufacturing step thereof;

[0140]FIGS. 30A and 30B are each a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 5 of the present invention;

[0141]FIG. 31 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 6 of the present invention;

[0142]FIG. 32 is a schematic cross-sectional view illustrating the semiconductor device according to Embodiment 6 of the present invention at a manufacturing step thereof;

[0143]FIG. 33 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 32;

[0144]FIG. 34 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 33;

[0145]FIG. 35 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following that of FIG. 34;

[0146]FIG. 36 is a schematic cross-sectional view illustrating a modification example of Embodiment 6 of the present invention;

[0147]FIG. 37 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 7 of the present invention;

[0148]FIG. 38 is a schematic cross-sectional view of the semiconductor device according to Embodiment 7 of the present invention at a manufacturing step thereof;

[0149]FIG. 39 is a schematic cross-sectional view of the semiconductor device at a manufacturing step following FIG. 38;

[0150]FIG. 40 is a schematic cross-sectional view illustrating a modification example of Embodiment 7 of the present invention;

[0151]FIG. 41 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 8 of the present invention;

[0152]FIG. 42 is a schematic plane view illustrating the rough constitution of a semiconductor device according to Embodiment 9 of the present invention;

[0153]FIG. 43 is a schematic cross-sectional view taken along a line A-A of FIG. 42; and

[0154]FIG. 44 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 10 of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0155] Embodiments of the present invention will next be described in details based on accompanying drawings. In all the drawings for describing the embodiments, like members of a function will be identified by like reference numerals and overlapping descriptions will be omitted. In order to facilitate understanding of the drawing, some cross-sections are not hatched.

[0156] (Embodiment 1)

[0157] In Embodiment 1, application of the present invention to a semiconductor device having a complementary MISFET having a power-supply voltage of from 1 to 1.5V and a gate length of from 0.1 to 0.14 μm will be described.

[0158]FIG. 1 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 1 of the present invention,

[0159]FIG. 2 is a characteristic chart showing dependence, on film stress, of a percent variation in drain current,

[0160]FIGS. 3 and 4 are schematic plane view and schematic cross-sectional view illustrating the relationship between a current direction and a film stress direction, respectively;

[0161] FIGS. 5 to 19 are each a schematic cross-sectional view of a semiconductor device of FIG. 1 during at manufacturing steps thereof, and

[0162] FIGS. 20 to 23 are each a schematic cross-sectional view for explaining the problem found by the present inventors during the development of the present invention.

[0163] In FIG. 1 and FIGS. 5 to 19, an n channel conductivity type MISFET (n-type MISFET) is illustrated on the left side, while a p channel conductivity type MISFET (p-type MISFET) is illustrated on the right side.

[0164] As illustrated in FIG. 1, the semiconductor device according to this Embodiment has a semiconductor substrate composed mainly of a p type silicon substrate (which will hereinafter be called “p type substrate” simply) made of, for example, single crystal silicon. The circuit formation surface (one main surface) of the p type substrate 1 has, thereon, an nMIS formation region (first element formation region) in and a pMIS formation region (second element formation region) 1p and the nMIS formation region in is separated from the pMIS formation region 1p by an element isolation region such as an shallow groove isolation (SGI) region 4. In the nMIS formation region in, a p type well 2 and an n channel conductivity type MISFET (Which will hereinafter be called “n-type MISFET”, simply) are formed, while in the pMIS formation region 1p, an n type well region 3 and a p channel conductivity type MISFET (which will hereinafter be called “p-type MISFET”, simply) are formed. The shallow groove isolation region 4 is formed by making a shallow groove in the circuit formation surface of the p type substrate 1 and then selectively embedding inside of the shallow groove with an insulating film (for example, a silicon oxide film). The n-type and p-type MISFETS of this Embodiment each has a horizontal structure permitting flow of an electric current in the plane direction of the p type substrate 1.

[0165] The n-type MISFET has mainly a channel formation region, a gate insulating film 5, a gate electrode 6, sidewall spacers 9, a source region and a drain region. The source and drain regions have n type semiconductor regions (extension regions) 7 and n type semiconductor regions 10. The n type semiconductor regions 7 are formed in self alignment with the gate electrode 6, while the n type semiconductor regions 10 are formed in self alignment with the sidewall spacers 9 disposed on the sidewalls of the gate electrode 6. The n type semiconductor regions 10 are formed to have a higher impurity concentration than the n type semiconductor regions 7.

[0166] The p-type MISFET has mainly a channel formation region, a gate insulating film 5, a gate electrode 6, sidewall spacers 9, a source region and a drain region. The source and drain regions have p type semiconductor regions (extension regions) 8 and p type semiconductor regions 11. The p type semiconductor regions 8 are formed in self alignment with the gate electrode 6, while the p type semiconductor regions 11 are formed in self alignment with sidewall spacers 9 disposed on the sidewalls of the gate electrode 6. The p type semiconductor regions 11 are formed to have a higher impurity concentration than the p type semiconductor regions 8.

[0167] Over the surface of each of the gate electrode 6, n type semiconductor regions 10 and p type semiconductor regions 11, a silicide layer (metal.semiconductor reaction layer) 12 is formed in order to lower the resistance. The silicide layer 12 disposed over the surface of the gate electrode 6, the silicide layer disposed on the surface of each of the n type semiconductor regions 10 and p type semiconductor regions 11 is formed in self alignment with the sidewall spacers 9 disposed over the sidewalls of the gate electrode 6. These silicide layers 12 are formed, for example, by the salicide (Self Aligned Silicide) technique. The n-type and p-type MISFETS of this Embodiment each has a salicide structure.

[0168] Over the circuit formation surface of the p type substrate 1, an interlayer insulating film 16 is formed, for example, from a silicon oxide film. This interlayer insulating film 16 is formed to cover the circuit formation surface of the p type substrate 1. Between the n-type MISFET and interlayer insulating film 16, formed is, for example, a silicon nitride film 14 a which is a first nitride film serving to generate a tensile stress on the circuit formation surface of the p type substrate 1. Between the p type MISFET and interlayer insulating film 16, formed is, for example, a silicon nitride film 14 b which is a second nitride film serving to generate a compressive stress on the circuit formation surface of the p type substrate 1. In this Embodiment, the silicon nitride film 14 a is selectively formed over the n-type MISFET to cover its gate electrode 6, while the silicon nitride film 14 b is selectively formed over the p-type MISFET to cover its gate electrode 6.

[0169] Between the n-type MISFET and silicon nitride film 14 a, and between the p-type MISFET and silicon nitride film 14 b, an insulating film 13 made of, for example, a silicon oxide film is formed. This insulating film 13 is formed on the circuit formation surface of the p type substrate 1 to cover each of the n-type and p-type MISFETs.

[0170] Between the silicon nitride film 14 a and the interlayer insulating film 16, an insulating film 15 made of, for example, a silicon oxide film is formed. This insulating film 15 is formed over the silicon nitride film 14 a selectively to cover this silicon nitride film 14 a.

[0171] Over the n type semiconductor regions 10 and p type semiconductor regions 11, contact holes 18 for source-drain extending from the surface of the interlayer insulating film 16 to the silicide layer 12 are formed. Inside of these contact holes 18 for source-drain, a conductive plug 19 is embedded. The n type semiconductor regions 10 and p type semiconductor regions 11 are each electrically connected, via the silicide layer 12 and conductive plug 19, to an interconnect 20 which extends over the interlayer insulating film 16.

[0172] Although not illustrated, a contact hole for gate which hole extends from the surface of the interlayer insulating film 16 to the silicide layer 12 is formed over the gate electrode 6. A conductive plug 19 is embedded inside of this gate contact hole. The gate electrode 6 is electrically connected, via the silicide layer 12 and the conductive plug 19 inside of the gate contact hole, to an interconnect 20 extending over the interlayer insulating film 16.

[0173] The source-drain contact hole 18 and gate contact hole are each formed by the SAC (Self Aligned Contact Hole) technique using the silicon nitride films 14 a, 14 b as an etching stopper. In other words, the silicon nitride films 14 a, 14 b serve as an insulating film for self aligned contact.

[0174] These silicon nitride films 14 a, 14 b are formed, for example, by the plasma CVD (Chemical Vapor Deposition) method. The stress to be generated on the circuit formation surface of the p type substrate 1 can be controlled by changing the forming conditions of these silicon nitride films 14 a, 14 b (reactive gas, pressure, temperature, RF power, etc.). In this Embodiment, a stress generated on the circuit formation surface of the p type substrate 1 is controlled toward a tensile stress by forming the silicon nitride film 14 a under the conditions of an RF power lowered to a range of from 300 to 400 W. On the other hand, a stress generated on the circuit formation surface of the p type substrate 1 is controlled toward a compressive stress by forming the silicon nitride film 14 b under the conditions of an RF power heightened to a range of from 600 to 700W.

[0175] A tensile stress of from about +700 to +800 Mpa exists inn the silicon nitride film 14 a and a compressive stress of from about −900 to −1000 Mpa exists in the silicon nitride film 14 a, each formed in the above-described manner, so that a tensile stress appears in the channel formation region of the n-type MISFET and a compressive stress appears in the channel formation region of the p-type MISFET, resulting in a 10 to 15% improvement in the drain current of the n-type MISFET and a 15 to 20% improvement in the drain current of the p-type MISFET compared with the case not covered with the silicon nitride films 14 a, 14 b. As described above, these stresses are applied to a direction similar to that of the drain current (Id) flowing through the channel formation region (that is, gate length direction).

[0176] A stress appearing in the channel formation region of MISFET will next be described using a simplified drawing and reference numerals a little different from those of this Embodiment. The MISFET as illustrated in FIGS. 3 and 4 has a silicide structure similar to that of this Embodiment. Indicated at numeral 30 is the channel formation region of MISFET, 31 is the direction of a drain current flowing through the channel formation region 30, 32 is a semiconductor region formed in alignment with the gate electrode 6, 33 is a semiconductor region formed in alignment with the sidewall spacer 9, 34 is a film for generating a stress in the channel formation region 30, and 35 a and 35 b are each a step portion.

[0177] As illustrated in FIGS. 3 and 4, MISFET has sidewall spacers 9 disposed over the sidewalls of the gate electrode 6 to surround the gate electrode 6. The gate electrode 6 and sidewall spacers 9 protrude from the substrate so that step portions (35 a,35 b) resulting from them appear. When a film 34 is formed over the MISFET of such a structure to cover the gate electrode 6 in order to generate a stress (tensile stress or compressive stress) in the channel formation region 30, the stress concentrates on the foot of the step portion 35 a existing in the gate length direction X and the foot of the step portion 35 b existing in the gate width direction Y so that the film stress in the gate length direction which stress starts from the foot of the step portion 35 a existing in the gate length direction X acts on the channel formation region 30 and at the same time, the film stress in the gate width direction which stress starts from the foot of the step portion 35b existing in the gate width direction Y acts on the channel formation region 30. In other words, when the stress by the film 34 is a tensile stress, the tensile stress appears in the channel formation region 30 in the gate length direction and gate width direction, while when the stress by the film 34 is a compressive stress, the compressive stress appears in the channel formation region 30 in the gate length direction and gate width direction.

[0178] The length of the gate electrode 6 in the gate length direction X is by far smaller than its length in the gate width direction Y, so that tensile stress or compressive stress in the gate width direction which stress appears in the channel formation region 30 by a tensile stress or a compressive stress focused on the foot of the step portion 35 b in the gate width direction Y is markedly small. Accordingly, the stress appearing in the channel formation region 30 by the film 34 can be regarded substantially as only a tensile stress or compressive stress in the gate length direction, in other words, as a tensile stress or compressive stress along the drain current direction 31.

[0179] It is reported that in the p type MISFET, a decrease in the drain current occurs when a compressive stress in the gate width direction is applied on the channel formation region 30. With regards to the control, by the film 34, of a stress on the channel formation region 30, the drain current of the p-type MISFET can be increased efficiently, because as described above, the compressive stress in the gate width direction, which stress appears in the channel formation region 30, is markedly small. Stress control of the channel formation region 30 by the film 34 is therefore particularly effective for the p-type electric field transistor.

[0180] Since the stress caused in the channel formation region 30 by the stress of the film 34 decreases as the starting point of the film stress departs from the channel formation region 30, it is desired to place the starting point of the film stress close as possible to the channel formation region 30. In the above description, stress starts from the foot of the step portions (35 a, 35 b) resulting from the gate electrode 6 and sidewall spacers 9. In the case of MISFET without sidewall spacers 9, the foot of each of the sidewalls of the gate electrode 6 becomes a starting point of film stress.

[0181] The fabrication of the semiconductor device of Embodiment 1 will next be described based on FIGS. 5 to 19.

[0182] First, a p type substrate 1 made of single crystal silicon having a specific resistance of 10 106 cm is prepared and on the circuit formation surface of the p type substrate 1, a p type well region 2 and an n type well region 3 are formed selectively as illustrated in FIG. 5.

[0183] Then, as illustrated in FIG. 5, a shallow groove isolation region 4 is formed on the circuit formation surface of the p type substrate 1 as an element isolation region for separating an nMIS formation region (first element formation region) 1n from a PMIS formation region (second element formation region) 1p. This shallow groove isolation region 4 is formed by forming a shallow groove (for example, a groove of about 300 [nm] deep) on the circuit formation surface of the p type substrate 1, forming, for example, a silicon oxide film as an insulating film over the circuit formation surface of the p type substrate 1 by CVD, and then planarizing the insulating film to leave it only inside of the shallow groove by CMP (Chemical Mechanical Polishing).

[0184] As illustrated in FIG. 6, a gate insulating film 5 made of, for example, a silicon oxide film of about 2 to 3 nm thick is formed by heat treatment in the nMIS formation region in and PMIS formation region 1p on the circuit formation surface of the p type substrate 1. Then, a polycrystalline silicon film of about 150 to 200 nm thick is formed all over the circuit formation surface of the p type substrate 1 by CVD, followed by the formation of a gate electrode 6 by patterning of the polycrystalline silicon film. During or after deposition of the polycrystalline silicon film, an impurity to reduce a resistance is introduced therein.

[0185] As illustrated in FIG. 6, a pair of n type semiconductor regions (extension regions) 7 are formed by selectively introducing, by ion implantation, an impurity such as arsenic (As) into an area of the p type well region 2 free of the gate electrode 6, followed by the formation of a pair of p type semiconductor regions (extension regions) 8 by selectively introducing, by ion implantation, an impurity such as boron difluoride (BF₂) into an area of the n type well region 3 free of the gate electrode 6. The n type semiconductor regions 7 are formed while the pMIS formation region 1p is covered with a photoresist mask, while the p type semiconductor regions 8 are formed while the nMIS formation region 1n is covered with a photoresist mask. Arsenic is introduced under the conditions of an acceleration energy of 1 to 5 KeV and dose of 1 to 2×10¹⁵/cm². Boron difluoride is introduced under the conditions of an acceleration energy of 1 to 5 KeV and dose of 1 to 2×10¹⁵/cm². The n type semiconductor regions 7 and p type semiconductor regions 8 are each formed in alignment with the gate electrode 6.

[0186] After introduction of an impurity to form the semiconductor regions (7,8), these semiconductor regions (7,8) are activated by heat treatment.

[0187] As illustrated in FIG. 6, sidewall spacers 9 having, for example, a thickness in the gate length direction of about 50 to 70 nm thick are formed on the sidewalls of the gate electrode 6. These sidewall spacers 9 are formed by forming an insulating film made of, for example, silicon oxide film or silicon nitride film by CVD all over the circuit formation surface of the p type substrate 1 and then subjecting the insulating film to anisotropic etching such as RIE (Reactive Ion etching). These sidewall spacers 9 are formed in alignment with the gate electrode 6.

[0188] As illustrated in FIG. 6, a pair of n type semiconductor regions 10 are formed by selectively introducing, by ion implantation, an impurity such as arsenic (As) into an area of the p type well region 2 free of the gate electrode 6 and sidewall spacers 9, followed by the formation of a pair of p type semiconductor regions 11 by selectively introducing, by ion implantation, an impurity such as boron difluoride (BF₂) into an area of the n type well region 3 free of the gate electrode 6 and the sidewall spacers 9. The n type semiconductor regions 10 are formed while the PMIS formation region 1p is covered with a photoresist mask, while the p type semiconductor regions 11 are formed while the nMIS formation region 1n is covered with a photoresist mask. Arsenic is introduced under the conditions of an acceleration energy of 35 to 45 KeV and dose of 2 to 4×10¹⁵/cm². Boron difluoride is introduced under the conditions of an acceleration energy of 40 to 50 KeV and dose of 2 to 4×10¹⁵/cm². The n type semiconductor regions 10 and p type semiconductor regions 11 are each formed in alignment with the sidewall spacers 9.

[0189] After introduction of an impurity to form the semiconductor regions (10,11), these semiconductor regions (10,11) are activated by heat treatment.

[0190] By the above-described steps, a source region and a drain region having the n type semiconductor regions 7 formed in alignment with the gate electrode 6 and the n type semiconductor regions 10 formed in alignment with the sidwall spacers 9 are formed; and a source region and a drain region having the p type semiconductor regions 8 formed in alignment with the gate electrode 6 and the p type semiconductor regions 11 formed in alignment with the sidwall spacers 9 are formed. Thus, horizontal n-type and p-type MISFETs are formed.

[0191] After the surfaces of the gate electrode 6 and semiconductor regions (10,11) are exposed by removing a natural oxidation film, sputtering is conducted to form a cobalt (Co) film 12 a as a refractory metal film all over the circuit formation surface of the p type substrate 1 including these surfaces, as illustrated in FIG. 7. Then, as illustrated in FIG. 8, heat treatment is conducted to react silicon (Si) of the gate electrode 6 with Co of the cobalt film 12, thereby forming a silicide (CoSi_(x)) layer 12 as a metal.semiconductor reacted layer on the surface of the gate electrode 6; and at the same time, to react Si of the semiconductor regions (10,11) with Co of the cobalt film 12 a to form a silicide (CoSi_(x)) layer 12 on the surface of the semiconductor regions (10,11). As illustrated in FIG. 9, an unreacted portion of the cobalt film 12 a is selectively removed from a region in which no silicide layer 12 is formed, followed by activation of the silicide layer 12 by heat treatment.

[0192] By the above-described steps, the silicide layer 12 disposed over the surface of the gate electrode 6 and the silicide layer 12 disposed over the surface of the semiconductor regions (10,11) are formed in alignment with the sidewall spacers 9. Thus, n-type and p-type MISFETs having a salicide structure are formed.

[0193] As illustrated in FIG. 10, an insulating film 13 made of, for example, a silicon oxide film of about 5 to 10 nm thick is formed by CVD all over the circuit formation surface of the p type substrate 1 including the n-type and p-type MISFETs. By this step, the silicide layer 12 of the gate electrode 6, the silicide layer 12 of the semiconductor regions (10,11) and sidewall spacers 9 are covered with the insulating film 13.

[0194] As illustrated in FIG. 11, a silicon nitride film 14 a of about 100 to 120 nm thick is formed by plasma CVD as an insulating film all over the circuit formation surface of the p type substrate 1 including the n-type and p-type MISFETs. This silicon nitride film 14 a is formed under the condition of, for example, RF power of 350 to 400 W or chamber inner pressure of 300 to 350 Torr.

[0195] By the above-described step, the n-type and p-type MISFETs are covered with the silicon nitride film 14 a, while the silicide layer 12 of the gate electrode 6, the semiconductor regions (10,11) and sidewall spacers 9 are covered with the silicon nitride film 14 a via the insulating film 13.

[0196] As illustrated in FIG. 12, an insulating film 15 made of, for example, a silicon oxide film of about 50 nm thick is formed by CVD all over the circuit formation surface of the p type substrate 1 including the upper surfaces of the n-type and p-type MISFETs. By this step, the silicon nitride film 14 a is covered with the insulating film 15.

[0197] As illustrated in FIG. 13, a photoresist mask RM1 selectively covering the upper surface of the nMIS formation region in (n-type MISFET) is formed over the insulating film 15.

[0198] With this photoresist mask RM1 as an etching mask, the insulating film 15 and silicon nitride film 14 a are successively removed by etching from the upper surface of the pMIS formation region 1p (the upper surface of p-type MISFET). For the removal of the insulating film 15 and the silicon nitride film 14 a, wet etching and isotropic dry etching are employed, respectively.

[0199] By the above-described step, the silicon nitride film 14 a is selectively formed over the n-type MISFET so as to cover its gate electrode 6. Owing to the silicon nitride film 14 a selectively formed in the above-described manner, a tensile stress is generated selectively in the channel formation region of the n-type MISFET.

[0200] Also by this step, an inconvenience of inevitable etching of the silicide layer 12 over the surface of the gate electrode 6, the silicide layer 12 over the surface of the p type semiconductor region 11 and sidewall spacers 9 owing to the overetching upon removal can be suppressed because these silicide layers 12 and sidewall spacers 9 are covered with the insulating film 13. Tn short, the insulating film 13 plays a role of an etching stopper upon removal of the silicon nitride film 14 a.

[0201] Without the insulating film 13 in this step, a trouble happens owing to the overetching of the silicon nitride film 14 a upon removal. A detailed description will be made of this trouble later.

[0202] As illustrated in FIG. 15, after removal of the photoresist mask RMT, a silicon nitride film 14 b of about 100 nm thick is formed, as an insulating film, by plasma CVD all over the circuit formation surface of the p-type substrate 1 including the upper surface of the insulating film 15. This silicon nitride film 14 b is formed, for example, under the condition of RF power of 600 to 700 W or chamber inner pressure of 5 to 10 Torr.

[0203] By this step, the n-type and p-type MISFETS are covered with the silicon nitride film 14 b, while the silicon nitride film 14 a over the n-type MISFET is covered with the silicon nitride film 14 b via the insulating film 15.

[0204] As illustrated in FIG. 16, a photoresist mask RM2 for selectively covering the upper surface of the PMIS formation region 1p (p-type MISFET) is formed over the silicon nitride film 14 b.

[0205] With this photoresist mask RM2 as an etching mask, the silicon nitride film 14 b is removed by etching as illustrated in FIG. 17 from the upper surface of the nMIS formation region In (upper surface of the n-type MISFET). The silicon nitride film 14 b is removed by isotropic dry etching.

[0206] By this step, the silicon nitride film 14 b is selectively formed over the p-type MISFET so as to cover its gate electrode 6. Owing to the silicon nitride film 14 b selectively formed in such a manner, a compressive stress is generated selectively in the channel formation region of the p-type MISFET.

[0207] In this step, since the silicon nitride film 14 a over the n-type MISFET is covered with the insulating film 15, an inconvenience of removal of the silicon nitride film 14 a by overetching upon removal of the silicon nitride film 14 b can be suppressed. In short, the insulating film 15 plays a role of an etching stopper upon removal of the silicon nitride film 14 b.

[0208] After removal of the photoresist mask RM2, an interlayer insulating film 16 made of, for example, a silicon oxide film is formed by plasma CVD all over the circuit formation surface of the p type substrate 1 including the upper surfaces of the n-type and p-type MISFETS as illustrated in FIG. 18, followed by planarization of the surface of the interlayer insulating film 16 by CMP.

[0209] As illustrated in FIG. 18, an impurity 17 such as Ar, Ge, Si, As, Sb, In or BF₂ is introduced into the interlayer insulating film 16 to destroy the crystallinity in the interlayer insulating film 16. In this step, the stress of the interlayer insulating film 16 is relaxed so that the influence of the stress of the interlayer insulating film 16 on the channel formation region of MISFET can be suppressed. When the cross-section of the interlayer insulating film 16 is observed, the mark of the destruction remains clearly.

[0210] As illustrated in FIG. 19, source-drain contact holes 18 extending from the surface of the interlayer insulating film 16 to the silicide layer 12 are then formed over the semiconductor regions (11,12). These source-drain contact holes 18 are formed by the SAC technique using silicon nitride films (14 a, 14 b) as an etching stopper. Described specifically, photoresist masks having opening patterns for the contact holes are formed over the interlayer insulating film 16 at positions opposite to the semiconductor regions (10,11). With the photoresist masks as an etching mask, the interlayer insulating film 16, insulating film 15, silicon nitride films (14 a, 14 b) and insulating film 13 are etched successively by anisotropic etching. The etching of the interlayer insulating film 16 and insulating film 15 is conducted under conditions permitting them to have an etching selectivity over the silicon nitride films (14 a, 14 b). The silicon nitride films (14 a, 14 b) are etched under conditions permitting these films to have an etching selectivity over the insulating film 13. The insulating film 13 is etched under the conditions permitting it to have an etching selectivity over the silicide layer 12 and p type substrate 1. The insulating film 13 may be etched by the overetching upon removal of the silicon nitride films (14 a, 14 b).

[0211] In a similar manner to that employed for the formation of the source-drain contact holes 18, a gate contact hole extending from the surface of the interlayer insulating film 16 to the silicide layer 12 is formed over the gate electrode 6, which is not however illustrated.

[0212] A conductive plug 19 is then formed by embedding a conductive substance inside of the source-drain contact hole 18 and inside of the gate contact hole, followed by the formation of an interconnect 20 over the interlayer insulating film 16, whereby a structure as illustrated in FIG. 1 can be formed.

[0213] In the next place, the present invention will be described together with the problems found by the present inventors during development of the present invention.

[0214] Upon removal of the silicon nitride film 14 a over the p-type MISFET by anisotropic dry etching, a portion of the silicon nitride film 14 a remains on the sidewall of the sidewall spacers 9 as illustrated in FIG. 20, because the silicon nitride film 14 a extending along the sidewall of the sidewall spacers 9 seems substantially thick upon execution of the anisotropic dry etching. If the silicon nitride film 14 b is formed over the pMISFET without removing the portion of the silicon nitride film 14 a, the stress of the silicon nitride film 14 b concentrates on the foot of the step portion 35 a formed by the gate electrode 6, sidewall spacers 9 and the portion of the silicon nitride film 14 a as illustrated in FIG. 21, making the starting point of the stress of the silicon nitride film 14 b apart from the channel formation region of the p-type MISFET owing to the silicon nitride film 14 a remaining on the sidewall of the sidewall spacers 9, thereby reducing an effect of the stress of the silicon nitride film 14 b for generating a compressive stress in the channel formation. In addition, the silicon nitride film 14 a having a reverse stress action remains on the sidewall of the sidewall spacers 9 so that the effect of the silicon nitride film 14 b for generating a compressive stress in the channel formation region is reduced further. It is therefore effective to remove the silicon nitride film 14 a from the p-type MISFET by isotropic dry etching which is free from the formation of an etching remnant at the step portion.

[0215] Isotropic dry etching of the silicon nitride film 14 a from the upper portion of the p-type MISFET is however accompanied with another problem.

[0216] For isotropic etching of a silicon nitride film, a fluoride gas such as CF₄ or CF₆ is usually employed. Upon this isotropic etching, the silicon nitride film has an etching selectivity over a silicon oxide film or silicide layer, but does not have over silicon.

[0217] Upon isotropic plasma etching of the silicon nitride film 14 a, the silicon nitride film 14 a has an etching selectivity over sidewall spacers 9 made of a silicon oxide film, but they are etched a little by overetching upon removal of the silicon nitride film 14 a, whereby the whole film thickness of the sidewall spacers 9 decreases towards the gate electrode 6. The silicide layer 12 on the surface of the p type semiconductor regions 11 are formed in alignment with the sidewall spacers 9. By a retreat in the film thickness of the sidewall spacers due to overetching upon removal of the silicon nitride film 14 a, an exposed portion a1 of silicon is inevitably formed between the sidewall spacers 9 and the silicide layer 12. Upon isotropic plasma etching of the silicon nitride film, it has no etching selectivity over silicon so that the p type substrate 1 is etched from the exposed portion 1 a by overetching upon removal of the silicon nitride film 14 a, causing an inconvenience such as peeling of the gate electrode 6.

[0218] Upon isotropic plasma etching, the silicon nitride film 14 a has an etching selectivity over the silicide layer 12, but the silicide layer 12 is etched a little by the overetching upon removal of the silicon nitride film 14 a and the thickness of the silicide layer 12 decreases. The silicide layer 12 is disposed on the surface of the gate electrode 6 or on the surfaces of the p type semiconductor regions 11 in order to suppress an increase in gate resistance or an increase in a source-drain current due to miniaturization of MISFET. An effect of suppressing an increase in gate resistance or in a source-drain current caused by miniaturization of MISFET lowers inevitably when the thickness of the silicide layer 12 decreases owing to overetching upon removal of the silicon nitride film 14 a.

[0219] In the case of the p-type MISFET having a salicide structure, since the silicide layer 12 serves as an etching stopper, the polycrystalline silicon film below the silicide layer 12 of the gate electrode 6, and the p type semiconductor region 11 below the silicide layer 12 of the source-drain regions are not etched by overetching upon removal of the silicon nitride film 14 a. In the case of a structure free from the silicide layer 12 on the surface of the gate electrode 6 or on the surface of the p type semiconductor regions 11, on the other hand, the polycrystalline silicon film of the gate electrode 6 and the p type semiconductor region 11 of the source-drain regions are reduced in film thickness owing to etching, leading to an increase in the gate resistance and source-drain resistance. An increase in the gate resistance causes lowering in switching speed, while an increase in the source-drain resistance causes a deterioration in current driving capacity.

[0220] For the removal of the silicon nitride film 14 a from the upper surface of the p-type MISFET, isotropic dry etching which does not form an etching remnant at the step portion is effective, but the above-described problem must be resolved in order to remove the silicon nitride film 14 a by isotropic dry etching.

[0221] The investigation by the present inventors has. revealed that the problem relating to the retreat in the thickness of the sidewall spacers 9 can be overcome by, prior to formation of the silicon nitride film 14 a over the n-type and p-type MISFETs so as to cover their gate electrodes 6, covering at least the upper surface of the end portion of the silicide layer 12, on the side of the sidewall spacers, of the p type semiconductor regions 11 with an insulating film capable of serving as an etching stopper.

[0222] The problem relating to etching of the silicide layer 12 can be overcome by, prior to the formation of the silicon nitride film 14 a over the n-type and p-type MISFETs so as to cover their gate electrodes 6, covering the whole surface of the silicide layer 12 with an insulating film capable of serving as an etching stopper.

[0223] The problem relating to a structure having no silicide layer 12 can be overcome by, prior to the formation of the silicon nitride film 14 a over the n-type and p-type MISFETs so as to cover their gate electrodes 6, covering the surface of the gate electrode 6 and the surface of the p type semiconductor regions 11 with an insulating film capable of serving as an etching stopper.

[0224] As the insulating film, a film over which the silicon nitride film 14 a has an etching selectivity upon isotropic plasma etching thereof, for example, a silicon oxide film is desired.

[0225] In the above-described Embodiment 1, as illustrated in FIGS. 10 and 11, the insulating film 13 made of a silicon oxide film is formed by CVD prior to the formation of the silicon nitride film 14 a. When the insulating film 13 is formed by CVD, that is, deposition method, the silicide layer 12 on the surface of the gate electrode 6, the silicide layer 12 on the surface of the p type semiconductor regions 11, the end portion of the silicide layer 12 on the surface of the p type semiconductor regions 11, said end portion existing on the side of the sidewall spacers 9, and the sidewall spacers 9 can be covered with the insulating film 13.

[0226] Accordingly, the silicon nitride film 14 b is removed from the p-type MISFET while covering the silicide layer 12 on the surface of the gate electrodes 6, the silicide layer 12 on the surface of the p type semiconductor regions 11, the end portion of the silicide layer 12 on the surface of the p type semiconductor regions 11, said end portion existing on the side of the sidewall spacers 9, and the sidewall spacers 9 with the insulating film 13, so that the problems relating to the retreat in the thickness of the sidewall spacers 9 and etching of the silicide layer 12 can be overcome at the same time.

[0227] As described above, a tensile stress and a compressive stress are applied to the channel formation region of the n-type MISFET and the channel formation region of the p-type MISFET, respectively, resulting in an increase in the drain current in both the n-type MISFET and p-type MISFET according to the intensity of the stress working on the channel formation region of each of the n-type MISFET and p-type MISFET.

[0228] The stresses working on the channel formation regions of the n-type MISFET and p-type MISFET can be controlled respectively so that a ratio of the drain current between the n-type MISFET and the p-type MISFET can be controlled freely.

[0229] The drain current of the n-type MISFET and that of the p-type MISFET can be increased simultaneously, making it possible to attain speed up of a semiconductor device having n-type and p-type MISFETs.

[0230] The problems relating to the retreat in the thickness of the sidewall spacers 9 or etching of the silicide layer 12, which will otherwise occur upon removal of the silicon nitride film 14 a from the upper surface of the p-type MISFET by isotropic dry etching, can be overcome, making it possible to provide a semiconductor device having a high production yield and high reliability.

[0231] In order to change a film stress by changing the method of forming the silicon nitride film, any one of the below-described methods, as well as a method of changing an RF power, can be adopted.

[0232] (1) The raw material gas is changed. For the formation of the silicon nitride film 14 a, SiH₄, NH₃ and N₂ are used, while for the formation of the silicon nitride film 14 b, only SiH₄ and N₂ are used.

[0233] (2) The film formation temperature is changed. The temperature upon formation of the silicon nitride film 14 a is set higher than that of the silicon nitride film 14 b.

[0234] (3) The pressure is changed. The pressure upon formation of the silicon nitride film 14 a is set higher than that of the silicon nitride film 14 b.

[0235] Any two or three of the above-described methods may be used in combination. What is important is to adjust the stress of the silicon nitride film 14 a toward the side of a tensile stress and the stress of the silicon nitride film 14 b toward the side of a compressive stress.

[0236] When a single-wafer thermal CVD method is used for the formation of a silicon nitride film, the lower the pressure upon film formation or the higher the temperature upon film formation, the film stress can be leaned toward the side of a tensile stress. Such conditions are therefore suited for the formation of the silicon nitride film 14 a.

[0237]FIG. 24 is a schematic cross-sectional view of a semiconductor device, at a manufacturing step thereof, which is a modification example of Embodiment 1 of the present invention. In FIG. 24, the n-type MISFET is illustrated on the left side, while the p-type MISFET is illustrated on the right side.

[0238] In the description of Embodiment 1, the silicon nitride film 14 a was formed prior to the silicon nitride film 14 b, but as illustrated in FIG. 24, the silicon nitride film 14 b may be formed prior to the silicon nitride film 14 a. Also in such a case, a tensile stress and a compressive stress can be applied respectively to the channel formation regions of the n-type MISFET and p-type MISFET so that the drain currents of the n-type MISFET and p-type MISFET can be increased simultaneously.

[0239] By isotropic plasma etching while covering the silicide layer 12 on the surface of the gate electrode 6, the silicide layer on the surface of the n-type semiconductor regions 10, the end portion of the silicide layer 12 on the surface of the n type semiconductor regions 10, said end portion being on the side of the sidewall spacers 9, and the sidewall spacers 9 with the insulating film 13, the silicon nitride film 14 b can be removed from the upper surface of the n-type MTSFET without causing problems relating to the retreat in the thickness of the sidewall spacers 9 or etching of the silicide layer 12.

[0240] In Embodiment 1 and modification example of it, the insulating film 13 made of a silicon oxide film was used as an etching stopper upon removal of the silicon nitride film 14 a, but not only it but also another insulating film may be used insofar as it is a film over which the silicon nitride film 14 a has an etching selectivity upon isotropic etching.

[0241] (Embodiment 2)

[0242]FIG. 25 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 2 of the present invention.

[0243]FIGS. 26A, 26B and 27 are each a schematic cross-sectional view of the semiconductor device, at a manufacturing step thereof, according to Embodiment 2 of the present invention. In FIGS. 25 to 27, an n-type MISFET is illustrated on the lift side, while a p-type MISFET is illustrated on the right side.

[0244] As illustrated in FIG. 25, the semiconductor device of Embodiment 2 is similar to that of Embodiment 1 except that the insulating film 13 serving as an etching stopper is removed.

[0245] When the insulating film 13 is left as in Embodiment 1 (refer to FIG. 18), the stress of the silicon nitride films (14 a, 14 b) concentrates on the foot of the step portion 35 a defined by the gate electrode 6, sidewall spacers 9 and insulating film 13 and the starting point of the stress of the silicon nitride films (14 a, 14 b) departs from the channel formation region of MISFET by the insulating film 13 remaining on the sidewall of the sidewall spacers 9, resulting in a decrease in the effect of the stress of the silicon nitride films (14 a, 14 b) for generating a stress in the channel formation region. It is therefore desired to removed the insulating film 13 if possible.

[0246] When the silicon nitride film 14 a is formed prior to the silicon nitride film 14 b as in Embodiment 1, the insulating film 13 is necessary in the step of removing the silicon nitride film 14 a on the p-type MISFET. When the silicon nitride film 14 b is formed prior to the silicon nitride film 14 a as in the modification example of Embodiment 1, the insulating film 13 is necessary in the step of removing the silicon nitride film 14 b from the upper surface of the n-type MISFET. The insulating film 13 is therefore removed in consideration of these steps.

[0247] Upon formation of the silicon nitride film 14 a prior to the silicon nitride film 14 b, the insulating film 13 is removed from the upper surface of the n-type MISFET prior to the step of forming the silicon nitride film 14 a as illustrated in FIG. 26A, and it is removed from the upper surface of the p-type MISFET after the removal of the silicon nitride film 14 a from the upper surface of the p-type MISFET as illustrated in FIG. 26B, which corresponds to FIG. 13, and FIG. 27. In other words, as illustrated in FIGS. 26B and 27, the insulating film 13 on the p-type MISFET is removed after removal of the insulating film 15 and silicon nitride film 14 a from the upper surface of the p-type MISFET.

[0248] Upon formation of the silicon nitride film 14 b prior to the silicon nitride film 14 a, the insulating film 13 is removed from the upper surface of the p-type MISFET prior to the step of forming the silicon nitride film 14 b, and the insulating film 13 is removed from the upper surface of the n-type MISFET after removal of the silicon nitride film 14 b from the upper surface of the n-type MISFET. The removal of the insulating film 13 on the n-type MISFET is performed while covering the upper surface of the p-type MISFET with, for example, a photoresist mask, while the removal of the insulating film 13 on the p-type MISFET is performed while covering the upper surface of the n-type MISFET with, for example, a photoresist mask.

[0249] It is desired to employ isotropic dry etching, which does not leave any remnant on the step portion, for the removal of the insulating film from the upper surface of the n-type MISFET or p-type MISFET. As isotropic dry etching of the insulating film 13 made of a silicon oxide film, isotropic plasma etching using a CF₃ gas or a mixed gas of CF₄ with H₂ is usually employed. In this isotropic plasma etching, the insulating film 13 has a sufficient etching selectivity over silicon or a silicide layer so that the p type substrate 1, silicide layer 12, sidewall spacers 9 and the like are not etched excessively.

[0250] In Embodiment 2, the insulating film 13 was removed from the upper surface of each of the n-type MISFET and p-type MISFET, but it is possible to leave the insulating film 13 on either one of them.

[0251] (Embodiment 3)

[0252]FIG. 28 is a schematic cross-sectional view of a semiconductor device, at a manufacturing step thereof, according to Embodiment 3 of the present invention. In FIG. 28, illustrated on the left side is an n-type MISFET, while illustrated on the right side is a p-type MISFET.

[0253] In Embodiment 1, the insulating film 13 made of a silicon oxide film formed by the deposition method was used as an etching stopper upon removal of the silicon nitride film 14 a. In Embodiment 3, on the other hand, an insulating film 21 made of a silicon oxide film formed by the thermal oxidation method is used as an etching stopper upon removal of the silicon nitride film 14 a. The formation of the insulating film 21 by the thermal oxidation method is conducted after the step of forming the n-type and p-type MISFETs having a salicide structure but before the step of forming the silicon nitride films 14 a, 14 b.

[0254] By the thermal oxidation method, the insulating film 21 can be formed selectively so as to cover therewith the silicide layer 12 on the surface of the gate electrode 6, and the silicide layer 12 on the surface of the semiconductor regions (10,11). This insulating film 21 can therefore suppress an inconvenience which will otherwise occur upon removal of the silicon nitride films (14 a, 14 b) by isotropic dry etching even if the silicon nitride film 14 a is formed prior to the silicon nitride film 14 b as in Embodiment 1 or the silicon nitride film 14 b is formed prior to the silicon nitride film 14 a as in the modification example of Embodiment 1.

[0255] (Embodiment 4)

[0256]FIG. 29 is a schematic cross-sectional view of a semiconductor device, at a manufacturing step thereof, according to Embodiment 4 of the present invention. In FIG. 29, illustrated on the left side is an n-type MISFET, while illustrated on the right side is a p-type MISFET.

[0257] In Embodiment 1, the insulating film 13 made of a silicon oxide film formed by the deposition method was used as an etching stopper upon removal of the silicon nitride film 14 a. In this Embodiment 4, on the other hand, sidewall spacers 22 formed on the side walls of the sidewall spacers 9 using a silicon oxide film are employed as an etching stopper upon removal of the silicon nitride film 14 a. The sidewall spacers 22 are formed after the formation of the n-type and p-type MISFETs having a salicide structure but before the formation of the silicon nitride films 14 a, 14 b. Sidewall spacers 22 are formed in a similar manner to that employed for the formation of the sidewall spacers 9.

[0258] By forming the sidewall spacers 22 made of a silicon oxide film on the sidewalls of the sidewall spacers 9, the end portion of the silicide layer 12 on the surface of the semiconductor regions (10,11), said end portion being on the side of the sidewall spacers 9, and the sidewall spacers 9 can be covered with the sidewall spacers 22 so that an inconvenience which otherwise occur upon removal of the silicon nitride films (14 a, 14 b) by isotropic dry etching, particularly an inconvenience relating to the retreat in the thickness of the sidewall spacers can be suppressed even if the silicon nitride film 14 a is formed prior to the silicon nitride film 14 b as in Embodiment 1 or the silicon nitride film 14 b is formed prior to the silicon nitride film 14 a as in the modification example of

[0259] Embodiment 1.

[0260] In this Embodiment 4, the sidewall spacers 22 made of a silicon oxide film were used as an etching stopper upon removal of the silicon nitride films (14 a, 14 b). Not only them but also another insulating film may be employed insofar as it is a film over which the silicon nitride films (14 a, 14 b) have a sufficient etching selectivity.

[0261] (Embodiment 5)

[0262]FIGS. 30A and 30B are each a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 5 of the present invention. In FIGS. 30A and 30B, illustrated on the left side is an n-type MISFET, while illustrated on the right side is a p-type MISFET.

[0263] In Embodiment 1, the present invention was applied to a semiconductor device having a complementary MISFET having a salicide structure. In this Embodiment 5, on the other hand, the present invention is applied to a semiconductor device having a complementary MISFET without a silicide layer.

[0264] As illustrated in FIG. 30A, the semiconductor device of Embodiment 5 is similar to that of Embodiment 1 except for the structure of the n-type and p-type MISFETs. Described specifically, the n-type and p-type MISFETS of Embodiment 5 have a structure free of a silicide layer on the surface of the gate electrode and on the surface of the semiconductor regions (10,11).

[0265] The semiconductor device of Embodiment 5 is formed in a similar manner to that employed in Embodiment 1 except for the step of forming a silicide layer.

[0266] Upon removal of the silicon nitride film 14 a from the upper surface of the p-type MISFET by isotropic dry etching, the silicide layer 12 serves as an etching stopper when the p-type MISFET has a salicide structure as in Embodiment 1, making it possible to avoid etching of the polycrystalline silicon film below the silicide layer 12 of the gate electrode 6 or etching of the p-type semiconductor regions 11 below the silicide layer 12 in the source-drain regions owing to overetching. When the p-type MISFET has a structure free of the silicide layer 12 on the surface of the gate electrode 6 or on the surface of the p type semiconductor regions, the polycrystalline silicon film of the gate electrode 6 or the p type semiconductor regions 11 in the source-drain regions are etched inevitably as illustrated in FIG. 23.

[0267] Such a problem can be overcome by covering, prior to the formation of the silicon nitride film 14 a, the upper surfaces of the gate electrode 6 and the p type semiconductor regions 11 with the insulating film 13 serving as an etching stopper.

[0268] In this Embodiment 5, the insulating film 13 is employed as an etching stopper. This insulating film 13 is formed by the deposition method. The deposition method is capable of covering the upper surfaces of the gate electrode 6 and p type semiconductor regions 11 simultaneously with the insulating film 13, making it possible to suppress etching of the gate electrode 6 and p type semiconductor regions 11 at the same time.

[0269] In this Embodiment 5, the silicon nitride film 14 awas formed prior to the silicon nitride film 14 b. Similar effects are available even if the silicon nitride film 14 b is formed prior to the silicon nitride film 14 a.

[0270] In this Embodiment 5, the insulating film 13 was employed as an etching stopper, but similar effects are available even if an insulating film 21 formed by the thermal oxidation method is used as an etching stopper. Also in this Embodiment 5, the insulating film 13 serving as an etching stopper was not removed, but it may be removed as in Embodiment 2 as illustrated in FIG. 30B.

[0271] The MISFET of Embodiment 5 having no silicide layer is, for example, formed, together with MISFET of any one of Embodiments 1 to 4 having a silicide layer, on one substrate, thereby constituting an MISFET and circuit which need a reduction in (junction) leakage current between the source region or drain region and the substrate. Described specifically, MISFET which needs a reduction in junction leakage current is constituted of MISFET of Embodiment 5 having no silicide layer, while MISFET which needs high-speed operation is constituted of MISFET of any one of Embodiments 1 to 4 having a silicide layer, whereby a decrease in power consumption and high-speed operation can be accomplished.

[0272] The insulating film 13 can be deposited in one step over MISFET having no silicide layer and MISFET having a silicide layer, making it possible to fabricate a semiconductor device featuring low power consumption and high-speed operation without increasing the number of the manufacturing steps.

[0273] When MISFET having a silicide layer and MISFET having no silicide layer are formed on one substrate, the former MISFET may be free of the insulating film 13 serving as an etching stopper as illustrated in FIG. 25, while the latter MISFET may have the insulating film 13 serving as an etching stopper as illustrated in FIG. 30A.

[0274] In the above-described case, the time when the insulating film 13 is removed from the upper surface of the MISFET having a silicide layer varies depending on which film is formed first, a first film for generating a stress in the channel formation region of MISFET having a silicide layer or a second film for generating a stress in the channel formation region of the MISFET free of the silicide layer. For example, supposing that the MISFET having a silicide layer is an n-type type and the MISFET having no silicide layer is a p-type type, when the first film (silicon nitride film 14 a) is formed first, the insulating film 13 over the MISFET having a silicide layer is removed selectively prior to the formation of the silicon nitride film 14 a as illustrated in FIG. 26 (refer to this drawing after the p-type MISFET on the right side is substituted with a p-type MISFET having no silicide layer). When the second film (silicon nitride film 14 b) is formed first, on the other hand, the insulating film 13 over the MISFET having a silicide layer is removed selectively after selective removal of the silicon nitride film 14 b from the upper surface of the MISFET having a silicide layer but prior to the formation of the silicon nitride film 14 a. When the MISFET having a silicide layer is a p-type type and the MISFET having no silicide layer is an n-type type, the insulating film 13 is selectively removed from the upper surface of the MISFET having a silicide layer in a similar manner. When the MISFET having a silicide layer and MISFET free of a silicide layer are formed on the same substrate, an insulating film serving as an etching stopper may be omitted as illustrated in FIG. 25 in the case of MISFET having a silicide layer and as illustrated in FIG. 30B in the case of MISFET free of a silicide layer. By making a step of removing the insulating film 13 common to the MISFET having a silicide layer and MISFET free of a silicide layer, the removal of the insulating film can be carried out by the same number of steps as shown in Embodiment 2 so that the number of manufacturing steps can be reduced.

[0275] (Embodiment 6)

[0276]FIG. 31 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 6 of the present invention. FIGS. 32 to 35 are each schematic cross-sectional view of the semiconductor device, at a manufacturing step thereof, according to Embodiment 6 of the present invention. In FIGS. 31 to 35, illustrated on the left side is the n-type MISFET, while illustrated on the right side is the p-type MISFET.

[0277] In Embodiment 6, a film for generating a compressive strength in the channel formation region of the p-type MISFET is stacked over a film for generating a tensile strength in the channel formation region of the n-type MISFET, thereby increasing a drain current of each of the n-type and p-type MISFETs.

[0278] As illustrated in FIG. 31, the n-type and p-type MISFETs are each covered with the silicon nitride film 14 a, while the p-type MISFET is covered with the silicon nitride film 14 b. In other words, only the silicon nitride film 14 a exists on the n-type MISFET, while the silicon nitride films 14 a, 14 b exist on the p-type MISFET.

[0279] Since only the silicon nitride film 14 a exists on the n-type MISFET, only a tensile stress of the silicon nitride film 14 a is applied to the channel formation region of the n-type MISFET, while both a tensile stress of the silicon nitride film 14 a and compressive stress of the silicon nitride film 14 a are applied to the channel formation region of the p-type ISFET because the silicon nitride films 14 a, 14 b exist on the p-type MISFET. Accordingly, it is possible to generate a compressive stress in the channel formation region of the p-type MISFET by using at least the silicon nitride film 14 b having a compressive stress larger in terms of an absolute value than tensile stress of the silicon nitride film 14 a.

[0280] In Embodiment 6, the silicon nitride film 14 b having a compressive stress is formed above the silicon nitride film 14 a having a tensile stress so that the starting point of the film stress to the channel formation region of the p-type MISFET becomes farther in the silicon nitride film 14 a than in the silicon nitride film 14 a. In such a case, it is therefore desired to use the silicon nitride film 14 b having at least twice as much as a tensile stress, in terms of absolute value, of the silicon nitride film 14 a.

[0281] The manufacturing process of the semiconductor device according to Embodiment 6 will next be described based on FIGS. 32 to 35.

[0282] As illustrated in FIG. 32, n-type and p-type MISFETS having a salicide structure are formed in a similar manner to that employed in Embodiment 1.

[0283] As illustrated in FIG. 33, a silicon nitride film 14 a of about 100 to 120 nm thick is then formed by plasma CVD all over the circuit formation surface of a p type substrate 1 including the upper surfaces of n-type and p-type MISFETs. This silicon nitride film 14 a is formed, for example, under the condition of an RF power ranging from 350 to 400 W.

[0284] As illustrated in FIG. 34, an insulating film 15 made of, for example, a silicon oxide film of about 50 nm thick is formed by CVD all over the surface of the p type substrate 1 including the upper surfaces of the n-type and p-type MISFETS, followed by the formation of a silicon nitride film 14 b of about 100 to 200 nm thick by plasma CVD all over the surface of the p type substrate 1 including the upper surfaces of the n-type and p-type MISFETs. The silicon nitride film 14 b is formed, for example, under the condition of an RF power ranging from 600 to 700 W.

[0285] In the above-described step, the silicon nitride film 14 b having a compressive stress at least greater in terms of absolute value than a tensile stress of the silicon nitride film 14 a is formed so as to generate a compressive stress in the channel formation region of the p-type MISFET. In this Embodiment, the silicon nitride film 14 b was formed to have at least twice, in terms of absolute value, as much as that of a tensile stress of the silicon nitride film 14 a.

[0286] Over the silicon nitride film 14 b, a photoresist mask RM3 is formed to selectively cover therewith the upper surface of the p-type MISFET, followed by etching with the photoresist mask RM3 as an etching mask to remove the silicon nitride film 14 b over the n-type MISFET as illustrated in FIG. 35. The silicon nitride film 14 b is removed by isotropic dry etching.

[0287] The photoresist mask RM3 is then removed to give the structure as illustrated in FIG. 31.

[0288] As described above, a compressive stress can be generated in the channel formation region of the p-type MISFET by forming the silicon nitride film 14 a over the n-type and p-type MISFETs and then selectively forming the silicon nitride film 14 b having a compressive stress greater in terms of absolute value than a tensile stress of the silicon nitride film 14 a over the p-type MISFET. In this Embodiment, it is therefore possible to increase drain currents of the n-type MISFET and the p-type MISFET simultaneously.

[0289] In this Embodiment 6, since the silicon nitride film 14 a over the p-type MISFET is not removed, formation of the insulating film 13 serving as an etching stopper as in Embodiment 1 is not necessary. Compared with Embodiment 1, the number of manufacturing steps can therefore be reduced.

[0290] In this Embodiment 6, the formation of the silicon nitride film 14 a covering the n-type and p-type MISFETs was followed by the formation of the silicon nitride film 14 b covering only the upper surface of the p-type MISFET. The silicon nitride film 14 b covering only upper surface of the p-type MISFET may be formed prior to the formation of the silicon nitride film 14 a covering the upper surface of the n-type and p-type MISFETs. In this case, however, an insulating film serving as an etching stopper becomes necessary upon removal of the silicon nitride film 14 b as in Embodiment 1.

[0291]FIG. 36 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device which is a modification example of Embodiment 6 of the present invention. In FIG. 36, the n-type MISFET is illustrated on the left side, while the p-type MISFET is illustrated on the right side.

[0292] In Embodiment 6, the drain currents of the n-type and p-type MISFETs were increased simultaneously by forming over the n-type and p-type MISFETs the silicon nitride film 14 a having a tensile stress, and then selectively forming, over the p-type MISFET, the silicon nitride film 14 b having a compressive stress greater in terms of absolute value than a tensile stress of the silicon nitride film 14 a. As illustrated in FIG. 36, after formation of the silicon nitride film 14 b having a compressive stress over the n-type and p-type MISFETs, the silicon nitride film 14 a having a tensile stress greater in terms of absolute value than a compressive stress of the silicon nitride film 14 b may be selectively formed over the n-type MISFET. In this case, the drain currents of the n-type MISFET and p-type MISFET can be increased simultaneously.

[0293] In FIG. 36, the formation of the silicon nitride film 14 b covering the upper surfaces of the n-type and p-type MISFETs was followed by the formation of the silicon nitride film 14 a covering only the upper surface of the n-type MISFET. The silicon nitride film 14 a covering only the upper surface of the n-type MISFET may be formed prior to the formation of the silicon nitirde film 14 b covering the upper surfaces of the n-type and p-type MISFETs. In this case, however, an insulating film serving as an etching stopper upon removal of the silicon nitride film 14 b becomes necessary as in Embodiment 1.

[0294] (Embodiment 7)

[0295]FIG. 37 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 7 of the present invention. FIGS. 38 and 39 are each a schematic cross-sectional view of the semiconductor device, at a manufacturing step thereof, according to Embodiment 7 of the present invention. In FIGS. 37 to 39, a n-type MISFET is illustrated on the left side, while a p-type MISFET is illustrated on the right side.

[0296] This Embodiment 7 aims at an increase in the drain currents of the n-type and p-type MISFETs by the use of one silicon nitride film.

[0297] As illustrated in FIG. 37, the n-type and p-type MISFETs are covered with a silicon nitride film 24. This silicon nitride film 24 has two portions, that is, a first portion 24 a for generating a tensile stress in the channel formation region of the n-type MISFET and a second portion 24 b for generating a compressive stress in the channel formation region of the p-type MISFET. The first portion 24 a is formed over the n-type MISFET to cover its gate electrode 6, while the second portion 24 b is formed over the p-type MISFET to cover its gate electrode 6. The second portion 24 b is higher than the first portion 24 a in the concentrations of Si and N. The manufacturing process of the semiconductor device of this Embodiment 7 will next be described based on FIGS. 38 and 37.

[0298] After formation of the n-type and p-type MISFETS having a salicide structure in a similar manner to Embodiment 1, a silicon nitride film 24 for generating a tensile stress in the channel formation region of the n-type MISFET is formed, as illustrated in FIG. 38, by plasma CVD all over the circuit formation surface of the p type substrate 1 including the upper surfaces of the n-type and p-type MISFETS. The silicon nitride film 24 is formed, for example, under the condition of an RF power ranging from 350 to 400 W.

[0299] A photoresist mask RM4 covering the n-type MISFET and having an opening over the p-type MISFET is formed over the silicon nitride film 24. With the photoresist mask RM4 as a mask, Si and N are introduced, as illustrated in FIG. 39 by the ion implantation method, into the silicon nitride film 24 (into the silicon nitride film 24 over the p-type MISFET) exposed from the photoresist mask RM4. To attain introduction of these elements uniformly in the film depth direction, this ion implantation is conducted under the conditions of an acceleration energy permitting the peak value (Rp) of the element concentration in the depth direction to be about half of the film thickness and a dose of 1×10¹⁵/cm².

[0300] By the above-described step, the silicon nitride film 24 having the first portion 24 a, and the second portion 24 b higher in element concentration than the first portion 24 a is formed.

[0301] After removal of the photoresist mask RM4, the second portion 24 b of the silicon nitride film 24 is activated by heat treatment.

[0302] By this step, the second portion 24 b of the silicon nitride film 24 undergoes volume expansion and is converted into a film generating a compressive stress in the channel formation region of the p-type MISFET. As a result, as illustrated in FIG. 37, the silicon nitride film 24 has the first portion 24 a for generating a tensile stress in the channel formation region of the n-type MISFET and a second portion 24 b for generating a compressive stress in the channel formation region of the p-type MISFET.

[0303] By forming the silicon nitride film 24 to have the above-described structure, the drain currents of the n-type MISFET and p-type MISFET can be increased simultaneously also in Embodiment 7.

[0304] Moreover, in Embodiment 7, the silicon nitride film 24 over the p-type MISFET is not removed so that the formation of the insulating film 13 serving as an etching stopper as in Embodiment 1 is not necessary. The number of the manufacturing steps can therefore be decreased compared with that of Embodiment 1.

[0305] Furthermore, in Embodiment 7, the drain currents of the n-type and p-type MISFETs can be controlled simultaneously to show an increase by one silicon nitride film 24 so that it is necessary to carry out a covering step with a silicon nitride film only once. Compared with Embodiment 1, the covering step with a silicon nitride film and its removal step can be omitted, leading to simplification of the manufacturing steps.

[0306]FIG. 40 is a schematic cross-sectional view of a semiconductor device, at a manufacturing step thereof, according to a modification example of Embodiment 7 of the present invention.

[0307] In Embodiment 7, elements, that is, Si and N were introduced perpendicularly to the p type substrate 1. As illustrated in FIG. 40, they may be introduced obliquely to the p type substrate 1. In this case, elements can be introduced also into the gate sidewall portion (step portion) of the silicon nitride film 24 covering the sidewalls of the sidewall spacers 9, which brings about an improvement in the compressive stress generating effect.

[0308] (Embodiment 8)

[0309]FIG. 41 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 8 of the present invention.

[0310] In Embodiment 8, the present invention is applied to a semiconductor device having a complementary MISFET of a vertical double gate structure.

[0311] As illustrated in FIG. 41, the semiconductor device of Embodiment 8 is composed mainly of a semiconductor substrate (which will hereinafter be called “substrate”, simply) having an SOI (Silicon On Insulator) structure. The substrate 40 has, for example, a semiconductor layer 40 a, an insulating layer 40 b disposed over the semiconductor layer 40 a, and a semiconductor layer 40 c disposed over the insulating layer 40 b. The semiconductor layers 40 a and 40 c are each made of, for example, single crystal silicon, while the insulating layer 40 b is made of, for example, silicon oxide.

[0312] The semiconductor layer 40 c is divided into a plurality of element formation portions. Each element formation portion has either an n-type MISFET or p-type MISFET. In the semiconductor layer 40 c on which the n-type MISFET is to be formed, a p type well region 2 is disposed, while the semiconductor layer 40 c on which the p-type MISFET is to be formed, an n type well region 8 is disposed. Each of the semiconductor layers 40 c is encompassed with an insulating film 41 disposed over the insulating film 40 b, whereby they are separated and electrically isolated.

[0313] The n-type and p-type MISFETs of this Embodiment 8 have a double gate structure in which the semiconductor layer 40 c to be used as a channel formation region is sandwiched, in the plane direction (surface direction) of the substrate 40, by two gate electrodes 6. In addition, the n-type and p-type MISFETS have a vertical structure permitting flow of a drain current in the thickness direction of the substrate 40.

[0314] The silicon nitride film 14 a for generating a tensile stress in the channel formation region of the n-type MISFET is formed over the n-type MISFET to cover these two gate electrodes, 6, while the silicon nitride film 14 b for generating a compressive stress in the channel formation region of the p-type MISFET is formed over the p-type MISFET to cover the two gate electrodes 6.

[0315] In Embodiment 8, the n-type and p-type MISFETs have a double gate structure in which the semiconductor layer 40 c used as a channel formation region is sandwiched, in the plane direction of the substrate 40, by two gate electrodes 6, which doubles the influence of the stress caused by the silicon nitride film and heightens a drain current increasing ratio compared with the conventional type having a single gate structure.

[0316] (Embodiment 9)

[0317]FIG. 42 is a schematic plane view illustrating the rough constitution of a semiconductor device according to Embodiment 9 of the present invention, and FIG. 43 is a schematic cross-sectional view taken along a line A-A of FIG. 42.

[0318] In Embodiment 9, the present invention is applied to a semiconductor device having a complementary MISFET of a horizontal double gate structure.

[0319] As illustrated in FIGS. 42 to 43, n-type and p-type MISFETs of this Embodiment 9 have a double gate structure in which a semiconductor layer 40 c to be used as a channel formation region is sandwiched, in the plane direction of a substrate 40, by two gate electrodes 6. The n-type and p-type MISFETs have a horizontal structure permitting flow of a drain current in the plane direction of the semiconductor substrate 40.

[0320] The silicon nitride film 14 a for generating a tensile stress in the channel formation region of the n-type MISFET is formed over the n-type MISFET to cover two gate electrodes 6 thereof, while the silicon nitride film 14 b for generating a compressive stress in the channel formation region of the p-type MISFET is formed over the p-type MISFET to cover two gate electrodes 6 thereof.

[0321] In Embodiment 9, the double gate structure of the n-type and p-type MISFETs in which the semiconductor layer 40 c to be used as a channel formation region is sandwiched, in the plane direction of the substrate 40, by two gate electrodes 6 doubles the influence of the stress caused by the silicon nitride film and heightens a drain current increasing ratio compared with the conventional type having a single gate structure.

[0322] (Embodiment 10)

[0323]FIG. 44 is a schematic cross-sectional view illustrating the rough constitution of a semiconductor device according to Embodiment 10 of the present invention.

[0324] In Embodiment 10, the present invention is applied to a semiconductor device having a complementary MISFET of a horizontal double gate structure.

[0325] As illustrated in FIG. 44, the semiconductor device according to Embodiment 10 is composed mainly of a p type substrate 1. Over the main surface of the p type substrate 1, a semiconductor layer 42 is disposed. This semiconductor layer 42 is divided into a plurality of element formation portions and each portion has either an n-type MISFET or p-type MISFET. In the semiconductor layer 42 on which the n-type MISFET is to be formed, a p type well region 2 is disposed, while in the semiconductor layer 42 on which the p-type MISFET is to be formed, an n-type well region 3 is disposed. The semiconductor layers 42 are each encompassed by an insulating film 41 disposed over the p type substrate 1 and they are separated and electrically isolated.

[0326] The n-type and p-type MISFETs of this Embodiment 10 have a double gate structure in which the semiconductor layer 42 to be used as a channel formation region is sandwiched by two gate electrodes 6 in the thickness direction of the p type substrate 1. In addition, the n-type and p-type MISFETs have a horizontal structure permitting flow of a drain current in the plane direction of the substrate 40.

[0327] The n-type MISFET is sandwiched, in the thickness direction of the p type substrate 1, by two silicon nitride films 14 a for generating a tensile stress in its channel formation region. One of the silicon nitride films 14 a is disposed between the p type substrate 1 and the n-type MISFET, while the other one is disposed to cover therewith the upper surface of the n-type MISFET.

[0328] The p-type MISFET is sandwiched, in the thickness direction of the p type substrate 1, by two silicon nitride films 14 b for generating a compressive stress in its channel formation region. One of the silicon nitride films 14 b is disposed between the p type substrate 1 and the p-type MISFET, while the other one is disposed to cover therewith the upper surface of the p-type MISFET.

[0329] In Embodiment 10, the n-type and p-type MISFET have a double gate structure in which the semiconductor layer 40 c to be used as a channel formation region is sandwiched two gate electrodes 6 in the depth direction of the substrate 40. In addition, covering with two silicon nitride films doubles the influence of the stress caused by the silicon nitride film and heightens a drain current increasing ratio compared with the conventional type having a single gate structure.

[0330] The invention made by the present inventors were described specifically based on Embodiments. It is needless to say the present invention is not limited to or by these Embodiments and it can be changed within a range not departing from the gist of the invention.

[0331] For example, application of the structure of the present invention to the peripheral circuit or logic circuit of at least the memory system of the products having a memory system such as SRAM (Static Random Access Memory), DRAM (Dynamic Random Access Memory) and flash memory, higher-performance memory products are available.

[0332] Advantages available by the typical inventions disclosed by the present application will next be described.

[0333] The present invention makes it possible to increase a drain current (to improve a current driving capacity) of an n-channel conductivity type electric field transistor and a p-channel conductivity type electric field transistor.

[0334] The present invention makes it possible to freely set a drain current ratio between an n-channel conductivity type electric field transistor and a p-channel conductivity type electric field transistor. 

What is claimed is:
 1. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: (a) forming, over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, a first insulating film for generating a tensile stress in a channel formation region of said n-channel conductivity type field effect transistor so as to cover gate electrodes of said transistors, while covering, with an insulating film, a semiconductor region between the gate electrode of said p-channel conductivity type field effect transistor and an element isolation region of said semiconductor substrate; (b) selectively removing said first insulating film from the upper surface of said p-channel conductivity type field effect transistor by etching; (c) forming, over said n-channel conductivity type field effect transistor and said p-channel conductivity type field effect transistor, a second insulating film for generating a compressive stress in a channel formation region of said p-channel conductivity type field effect transistor so as to cover the gate electrodes of said transistors; and (d) selectively removing said second insulating film from the upper surface of the n-channel conductivity type field effect transistor.
 2. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: (a) forming, over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, a first insulating film for generating a compressive stress in a channel formation region of said p-channel conductivity type field effect transistor so as to cover gate electrodes of said transistors, while covering, with an insulating film, a semiconductor region between the gate electrode of said n-channel conductivity type field effect transistor and an element isolation region of said semiconductor substrate; (b) selectively removing said first insulating film from the upper surface of said n-channel conductivity type field effect transistor by etching; (c) forming, over said n-channel conductivity type field effect transistor and said p-channel conductivity type field effect transistor, a second insulating film for generating a tensile stress in a channel formation region of said n-channel conductivity type field effect transistor so as to cover the gate electrodes of the transistors; and (d) selectively removing said second insulating film from the upper surface of the p-channel conductivity type field effect transistor.
 3. A method according to claim 1, wherein the insulating film covering said semiconductor region includes sidewall spacers formed on the sidewalls of each of said gate electrodes and a deposited film formed to cover said sidewall spacers.
 4. A method according to claim 1, wherein the insulating film covering said semiconductor region includes sidewall spacers formed on the sidewalls of each of said gate electrodes and a deposited film formed to cover said sidewall spacers, and wherein a metal.semiconductor reacted layer formed in alignment with said sidewall spacers is disposed over the surface of said semiconductor region.
 5. A method according to claim 1, wherein the insulating film covering said semiconductor region includes sidewall spacers formed on the sidewalls of each of said gate electrodes and a thermally oxidized film formed between said sidewall spacers and said element isolation region.
 6. A method according to claim 1, wherein the insulating film covering said semiconductor region includes sidewall spacers formed on the sidewalls of each of said gate electrodes and a thermally oxidized film formed between said sidewall spacers and said element isolation region, and wherein a metal.semiconductor reacted layer formed in alignment with said sidewall spacers is disposed over the surface of said semiconductor region.
 7. A method according to claim 1, wherein said step (b) is carried out by isotropic etching.
 8. A method according to claim 1, wherein said step (d) is carried out by isotropic etching.
 9. A method according to claim 1, wherein said first and second insulating films are each an insulating film for self-aligning contact made of a silicon nitride film .
 10. A method according to claim 1, further comprising a step of forming an insulating film over said first insulating film after said step (a) but before said step (b), said step (b) including a step of selectively removing said insulating film from the upper surface of said p-channel conductivity type field effect transistor.
 11. A method according to claim 1, wherein the insulating film covering said semiconductor region includes sidewall spacers formed on the sidewalls of each of said gate electrodes and a deposited film formed to cover said sidewall spacers, and wherein said method further comprises removing said deposited film on the side of said p-channel conductivity type field effect transistor after said step (b) but before said step (c).
 12. A method according to claim 1, wherein the insulating film covering said semiconductor region includes sidewall spacers formed on the sidewalls of each of said gate electrodes and a deposited film formed to cover said sidewall spacers, and wherein said method further comprises removing said deposited film on the side of said n-channel conductivity type field effect transistor after the step of forming said deposited film but before said step (a).
 13. A method according to claim 2, further comprising the step of forming an insulating film over said first insulating film after said step (a) but before said step (b), said step (b) including a step of selectively removing said insulating film from the upper surface of said n-channel conductivity type field effect transistor.
 14. A method according to claim 2, wherein the insulating film covering said semiconductor region includes sidewall spacers formed on the sidewalls of each of said gate electrodes, and a deposited film formed to cover said sidewall spacers, and wherein said method further comprises removing said deposited film on the side of said n-channel conductivity type electric field transistor after said step (b) but prior to said step (c).
 15. A method according to claim 2, wherein the insulating film covering said semiconductor region includes sidewall spacers formed on the sidewalls of each of said gate electrodes, and a deposited film formed to cover said sidewall spacers, and wherein said method further comprises removing said deposited film on the side of said p-channel conductivity type electric field transistor after formation of said deposited film but prior to said step (a).
 16. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: (a) forming first sidewall spacers over a semiconductor region between each of gate electrodes of said n channel conductivity type and p channel conductivity type field effect transistors and an element isolation region of said semiconductor substrate in alignment with each of said gate electrodes; (b) forming, over the surface of said semiconductor region, a metal.semiconductor reacted layer in alignment with said first sidewall spacers; (c) forming second sidewall spacers over said metal.semicondutor reacted layer in alignment with said first sidewall spacers; (d) forming, over said n-channel conductivity type and p-channel conductivity type field effect transistor, a first insulating film for generating a tensile stress in a channel formation region of said n-channel conductivity type field effect transistor so as to cover gate electrodes of said transistors; (e) selectively removing said first insulating film from the upper surface of said p-channel conductivity type field effect transistor by etching; (f) forming, over said n-channel conductivity type and said p-channel conductivity type field effect transistors, a second insulating film for generating a compressive stress in a channel formation region of said p-channel conductivity type field effect transistor so as to cover the gate electrodes of said transistors; and (g) selectively removing said second insulating film from the upper surface of said n-channel conductivity type field effect transistor.
 17. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: (a) forming first sidewall spacers over a semiconductor region between each of gate electrodes of said n channel conductivity type and p channel conductivity type field effect transistors and an element isolation region of said semiconductor substrate in alignment with each of said gate electrodes; (b) forming, over the surface of said semiconductor region, a metal.semiconductor reacted layer in alignment with said first sidewall spacers; (c) forming second sidewall spacers over said metal.semicondutor reacted layers in alignment with said first sidewall spacers; (d) forming, over said n-channel conductivity type and p-channel conductivity type field effect transistors, a first insulating film for generating a compressive stress in a channel formation region of said p-channel conductivity type field effect transistor so as to cover the gate electrodes of said transistors; (e) selectively removing said first insulating film from the upper surface of said n-channel conductivity type field effect transistor by etching; (f) forming, over said n-channel conductivity type and said p-channel conductivity type field effect transistors, a second insulating film for generating a tensile stress in a channel formation region of said n-channel conductivity type field effect transistor so as to cover the gate electrodes of said transistors; and (g) selectively removing said second insulating film over the p-channel conductivity type field effect transistor.
 18. A method according to claim 16, wherein said step (e) is effected by isotropic etching.
 19. A method according to claim 16, wherein said first and second insulating films are each an insulating film made of a silicon nitride film for self-aligning contact.
 20. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: (a) forming, over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, a first insulating film having a tensile stress so as to cover the gate electrodes of said transistors; (b) forming, over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, a second insulating film having a compressive stress greater in terms of absolute value than a tensile stress of said first insulating film so as to cover the gate electrode of said transistors; and (c) selectively removing said second insulating film from the upper surface of said n-channel conductivity type field effect transistor by etching.
 21. A method according to claim 20, wherein the compressive stress of said second insulating film is at least twice as much as the tensile stress of said first insulating film.
 22. A method according to claim 20, wherein said step (c) is effected by isotropic etching.
 23. A method according to claim 20, wherein said step (a) is conducted prior to said step (b).
 24. A method according to claim 20, wherein said first and second insulating films are an insulating film made of a silicon nitride film for self-aligning contact.
 25. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: (a) forming a first insulating film having a compressive stress over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor so as to cover the gate electrode of said transistors; (b) forming a second insulating film having a tensile stress greater in terms of absolute value than a compressive stress of said first insulating film over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor so as to cover the gate electrode of said transistors; and (c) selectively removing said second insulating film from the upper surface of said p-channel conductivity type field effect transistor by etching.
 26. A method according to claim 25, wherein the tensile stress of said second insulating film is at least twice as much as the compressive stress of said first insulating film.
 27. A method according to claim 25, wherein said step (c) is performed by isotropic etching.
 28. A method according to claim 25, wherein said step (a) is performed prior to said step (b).
 29. A method according to claim 25, wherein said first and second insulating films are each an insulating film made of a silicon nitride film for self-aligning contact.
 30. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: forming an insulating film having a tensile stress over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor so as to cover the gate electrodes thereof; and introducing an element into said insulating film over said p-channel conductivity type field effect transistor, thereby converting said insulating film into a film capable of generating a compressive stress in the channel formation region of said p-channel conductivity type field effect transistor.
 31. A method according to claim 30, wherein the element is the same with an element contained in said insulating film.
 32. A method according to claim 30, wherein said conversion is effected by heat treatment after introduction of said element to cause volume expansion of said film.
 33. A method according to claim 30, wherein said insulating film is an insulating film made of a silicon nitride film for self-aligning contact.
 34. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: (a) forming, over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, a first insulating film for generating a tensile stress in the channel formation region of said n-channel conductivity type field effect transistor so as to cover the gate electrode of said transistors, while covering, with an insulating film, a semiconductor region between the gate electrode of said p-channel conductivity type field effect transistor and an element isolation region of said semiconductor substrate; and (b) selectively removing said first insulating film from the upper surface of said p-channel conductivity type field effect transistor by etching.
 35. A method according to claim 34, wherein said insulating film is a silicon oxide film, and wherein said first insulating film is an insulating film made of a silicon nitride film for self-aligning contact.
 36. A method of manufacturing a semiconductor device having an n-channel conductivity type field effect transistor and a p-channel conductivity type field effect transistor, each formed over a semiconductor substrate, comprising steps of: (a) forming, over said n-channel conductivity type field effect transistor and p-channel conductivity type field effect transistor, a first insulating film for generating a compressive stress in the channel formation region of said p-channel conductivity type field effect transistor so as to cover the gate electrode of said transistors, while covering, with an insulating film, a semiconductor region between the gate electrode of said n-channel conductivity type field effect transistor and an element isolation region of said semiconductor substrate; and (b) selectively removing said first insulating film from the upper surface of said n-channel conductivity type field effect transistor by etching.
 37. A method according to claim 36, wherein said insulating film is a silicon oxide film; and said first insulating film is an insulating film made of a silicon nitride film for self-aligning contact. 